PEEK

PEEK KetaSpire® PEEK KT-820GF30 SOLVAY USA

Properties:
high strengthChemical resistanceSteam sterilizationFatigue resistanceDimensional stabilityHigh temperature resistanHigh rigidity
Usages:
Laptop caseAircraft ApplicationsDental applicationsfilmAutomotive ApplicationsElectronic and Electrical Applications
Certificates:
UL
Compare View Prices

Technical Data Sheet

Filling analysis	Test Condition	Test Method	Test Result
Melt viscosity	400°C,1000sec^-1	ASTM D3835	850 Pa·s

impact performance	Test Condition	Test Method	Test Result
Suspended wall beam without notch impact strength	--	ISO 180	56 kJ/m²
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	--	ASTM D4812	960 J/m

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.6mm	UL 94	V-0
UL flame retardant rating	UL flame retardant rating	20.3mm	UL 94	V-0

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus	--5	ASTM D638	10500 Mpa
Tensile modulus	Tensile modulus	--	ISO 527-2/1A/1	11400 Mpa
tensile strength	Yield5	ASTM D638	158 Mpa
	tensile strength	Yield	ISO 527-2/1A/5	165 Mpa
	tensile strength	tensile strength	--	ASTM D638	158 Mpa
Nominal tensile fracture strain	--	ISO 527-2/1A/5	2.7 %
Nominal tensile fracture strain	Nominal tensile fracture strain	--6	ASTM D638	2.7 %
Bending modulus	--	ASTM D790	10300 Mpa
Bending modulus	Bending modulus	--	ISO 178	10700 Mpa
bending strength	--	ASTM D790	271 Mpa
	bending strength	--	ISO 178	246 Mpa
	bending strength	bending strength	Yield	ASTM D790	261 Mpa
compressive strength		ASTM D695	169 Mpa
shear strength		ASTM D732	93.1 Mpa
Poisson's ratio			7.58 0.34

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	1.8MPa,Annealed	ASTM D648	315 °C
Glass transition temperature		ASTM D3418	150 °C
Melting temperature		ASTM D3418	340 °C
Linear coefficient of thermal expansion	MD：-50to50°C	ASTME831	1.7E-05 cm/cm/°C
specific heat	50°C	DSC	1300 J/kg/°C
specific heat	specific heat	200°C	DSC	1730 J/kg/°C
thermal conductivity		ASTME1530	0.29 W/m/K

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate	400°C/2.16kg	ASTM D1238	0.70 g/10min
Shrinkage rate	MD:3.18mm	ASTM D955	0.20-0.40 %
Shrinkage rate	Shrinkage rate	TD:3.18mm	ASTM D955	1.4-1.6 %
Water absorption rate	24hr	ASTM D570	0.10 %

Electrical performance	Test Condition	Test Method	Test Result
Surface resistivity		ASTM D257	>1.9E+17 ohms
Volume resistivity		ASTM D257	1.9E+17 ohms·cm
Dielectric strength	3.00mm	ASTM D149	17 KV/mm
Dielectric constant	60Hz	ASTM D150	3.44
	Dielectric constant	1kHz	ASTM D150	3.44
	Dielectric constant	Dielectric constant	1MHz	ASTM D150	3.41
Dissipation factor	60Hz	ASTM D150	1E-03
	Dissipation factor	1kHz	ASTM D150	1E-03
	Dissipation factor	Dissipation factor	1MHz	ASTM D150	3E-03

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	M-Scale	ASTM D785	100
Shore hardness	ShoreD,1Sec	ASTM D2240	91

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.