PC/ABS MOCREATE® DCM01-4000P NINGBO ZHETIE DAFENG
48
- Properties:Easy electroplatingHigh temperature resistan
- Usages:Automotive sector
CompareTechnical Data Sheet
| other | Test Condition | Test Method | Test Result |
|---|---|---|---|
| characteristic | 电渡级.高流动.高抗冲 | ||
| Color | 本色 | ||
| purpose | 电器类.汽配 |
| processability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Dry conditions | 90-100度.4小时 | ||
| process temperature | 220-250 °C | ||
| 240-270 °C | |||
| 230-270 °C | |||
| Temperature | 50-100 °C | ||
| pressure | 30-80 Mpa | ||
| 40-120 Mpa |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| elongation at break | ASTM D638/ISO 527 | 60 % | |
| tensile strength | ASTM D638/ISO 527 | 43 kg/cm²(MPa)[Lb/in²] | |
| Flexural modulus | ASTM D790/ISO 178 | 2250 kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790/ISO 178 | 73 kg/cm²(MPa)[Lb/in²] |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.09 | |
| Shrinkage rate | ASTM D955 | 0.4-0.6 % | |
| melt mass-flow rate | ASTM D1238/ISO 1133 | 25 g/10min |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Combustibility (rate) | UL 94 | HB | |
| Heat distortion temperature | ASTM D648/ISO 75 | 90 ℃（℉） | |
| ASTM D648/ISO 75 | 110 ℃（℉） | ||
| vicat | ASTM D1525/ISO R306 | 112 ℃（℉） |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.