Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ASTM D1238 | 1.0 g/10min |
| melt mass-flow rate | | | 50.8 microns |
| processability | Test Condition | Test Method | Test Result |
|---|
| Melt Temperature | | | 232 °C |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| gloss | | ASTM D-2457 | 60 |
| Haze ratio | | ASTM D-1003 | 10 % |
| gloss | | ASTM2457 | 60 |
| Haze ratio | | ASTM D1003 | 10 % |
| Basic performance | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D-792 | 0.92 g/m3 |
| melt mass-flow rate | | ASTM D-1238 | 1 g/10min |
| film thickness | | | 50.8 um |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Secant modulus | | ASTM D-882 | 194 Mpa |
| Secant modulus | | ASTM D-882 | 233 Mpa |
| tensile strength | | ASTM D-882 | 10.9 Mpa |
| tensile strength | | ASTM D-882 | 12.3 Mpa |
| tensile strength | | ASTM D-882 | 55.1 Mpa |
| tensile strength | | ASTM D-882 | 49.8 Mpa |
| elongation at break | | ASTM D-882 | 890 % |
| elongation at break | | ASTM D-882 | 830 % |
| impact force | | | 235 ft-lbf/in3 |
| elongation | | ASTM D882 | 827 % |
| elongation | | ASTM D882 | 889 % |
| Elmendorf tear strength | | ASTM D192 | 902 g |
| Elmendorf tear strength | | ASTM D192 | 1200 g |
| Dart impact | | ASTM D1709 | 288 g |
| tensile strength | | ASTM D882 | 10.89 Mpa |
| tensile strength | | ASTM D882 | 12.29 Mpa |
| Secant modulus | | ASTM D882 | 194.4 Mpa |
| Secant modulus | | ASTM D882 | 232.6 Mpa |
| tensile strength | | ASTM D882 | 55.11 Mpa |
| tensile strength | | ASTM D882 | 49.81 Mpa |
| Other performance | Test Condition | Test Method | Test Result |
|---|
| Thin film puncture strength | | 内部方法 | 19.4 J/cm³ |
| Film toughness | | ASTM D-882 | 346 J/cm³ |
| Film toughness | | ASTM D-882 | 351 J/cm4 |
| Elmendorf tear strength | | ASTM D1922 | 17.8 g/micron |
| Elmendorf tear strength | | ASTM D1922 | 23.6 g/micron |
| impact force | | ASTM D882 | 4176 ft-lbf/in3 |
| impact force | | ASTM D882 | 4241 ft-lbf/in3 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| vicat | | ASTM D-1525 | 108 °C |
| melting temperature | | 内部方法 | 122 °C |
| vicat | | ASTM1525 | 108 °C |
| vicat | | 陶氏化学方法(DSC | 122 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.