PP CELSTRAN® GF30-0453
68
- Properties:Low warpageChemical couplingCreep resistanceHigh rigidityhigh strengthLow volatilityLow temperature impact re
- Usages:Automotive sector
Compare
View PricesTechnical Data Sheet
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1A | 7000 Mpa | |
| Tensile stress | ISO 527-2/1A/5 | 110 Mpa | |
| Tensile strain | ISO 527-2/1A/5 | 2.2 % | |
| Flexural modulus | ISO 178 | 7000 Mpa | |
| ISO 178 | 6600 Mpa | ||
| Bending stress | ISO 178 | 180 Mpa | |
| ISO 178 | 100 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO 179/1eU | 45 kJ/m² | |
| ISO 179/1eU | 55 kJ/m² |
| injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| drying temperature | 90 到 100 °C | ||
| drying time | 4.0 hr | ||
| Suggested maximum moisture content | 0.20 % | ||
| Temperature at the rear of the barrel | 220 到 230 °C | ||
| Temperature in the middle of the barrel | 230 到 240 °C | ||
| Temperature at the front of the material cylinder | 240 到 250 °C | ||
| Spray nozzle temperature | 240 到 250 °C | ||
| Processing (melt) temperature | 230 到 270 °C | ||
| Temperature | 30 到 70 °C | ||
| injection speed | 慢 | ||
| Back pressure | < 3.00 Mpa |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ISO 75-2/A | 158 °C | ||
| ISO 75-2/C | 122 °C | ||
| Melting temperature 2 | ISO 11357-3 | 166 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.