Technical Data Sheet
| Cured Properties | Test Condition | Test Method | Test Result |
|---|
| LapShearStrength | | | >11.0 MPa |
| | | 3.51 |
| Volume resistivity | | | 3E+11 ohms·cm |
| Dissipation Factor | | | 9E-03 |
| Supporting hardness | | | 60 |
| Uncured Properties | Test Condition | Test Method | Test Result |
|---|
| density | | | 2.0到7.0 Pa·s |
| density | | | >2.0 hr |
| density | Pot Life | | 180 min |
| colour | | | Clear/Transparent |
| colour | | | Grey |
| density | | | 0.958 g/cm³ |
| density | | | 1.65 g/cm³ |
| thermosetting | Test Condition | Test Method | Test Result |
|---|
| | | 按重量计算的混合比:14 |
| | | 52 wk |
| | | 按重量计算的混合比:100 |
| physical property | Test Condition | Test Method | Test Result |
|---|
| Particle size | | | <300 µm |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| DegradationTemperature | | TGA | 347 °C |
| Shear Strength | | | 23.4 MPa |
| Operating | | | -55到200 °C |
| Operating | | | -55到300 °C |
| Operating | | | 4.97 GPa |
| Operating | | | 1.53 |
| WeightLossonHeating | | | <0.050 % |
| WeightLossonHeating | | | 0.16 % |
| WeightLossonHeating | | | 1.0 % |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Glass Transition Temperature | | | >40.0 °C |
| | | 3.7E-05 cm/cm/°C |
| | | 1.5E-04 cm/cm/°C |
| Linear coefficient of thermal expansion | | | 2.0 W/m/K |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare