PC 302-5 STYRON US

Form：Granules | Grade：Injection grade

Properties:

heat-resistingoptical performance High impact resistance

Typical Applications:

sheetsheet

Supplier(0)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	sheet \| sheet
Properties:	heat-resisting \| optical performance \| High impact resistance

Certificates

No Data...

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result	Test Unit
turbidity		ASTM D1003	1.0	%
transmissivity		ASTM D1003	86.0to90.0	%
Refractive index		ISO 489	1.586
Refractive index	Refractive index		ASTM D542	1.586
impact performance	Test Condition	Test Method	Test Result	Test Unit
Charpy Notched Impact Strength	23°C	ISO 179/1eA	81	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	-30°C	ISO 179/1eA	71	kJ/m²
Impact strength of cantilever beam gap	23°C	ASTM D256	910	J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	-30°C	ASTM D256	590	J/m
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	3.0mm	UL 94	HB
UL flame retardant rating	UL flame retardant rating	1.5mm	UL 94	HB
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Taber wear resistance		ASTM D1044	5	%
bending strength		ISO 178	94.0	Mpa
bending strength	bending strength		ASTM D790	93.8	Mpa
elongation	Break	ASTM D638	170	%
Tensile strain	Yield	ISO 527-2/50	6.0	%
Bending modulus		ISO 178	2350	Mpa
Bending modulus	Bending modulus		ASTM D790	2340	Mpa
Tensile strain	Break	ISO 527-2/50	170	%
Tensile modulus		ASTM D638	2410	Mpa
Tensile modulus	Tensile modulus		ISO 527-2/50	2400	Mpa
tensile strength	Yield	ASTM D638	60.7	Mpa
	tensile strength	Yield	ISO 527-2/50	61.0	Mpa
		tensile strength	Break	ASTM D638	71.7	Mpa
		tensile strength	tensile strength	Break	ISO 527-2/50	72.0	Mpa
elongation	Yield	ASTM D638	6.0	%
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion	MD：-40to82°C	ASTM D696	6.8E-05	cm/cm/°C
Vicat softening temperature	--	ISO 306/B50	148	°C
	Vicat softening temperature	--	ISO 306/A120	154	°C
		Vicat softening temperature	--	ASTM D15257	154	°C
		Vicat softening temperature	Vicat softening temperature	--	ASTM D15256	148	°C
Glass transition temperature		ASTM D3418	150	°C
Glass transition temperature	Glass transition temperature		ISO 11357-2	150	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density		ASTM D792	1.20	g/cm³
density	density		ISO 1183/B	1.20	g/cm³
melt mass-flow rate	300°C/1.2kg	ASTM D1238	5.0	g/10min
melt mass-flow rate	melt mass-flow rate	300°C/1.2kg	ISO 1133	5.0	g/10min
Shrinkage rate	MD	ASTM D955	0.50-0.70	%
Shrinkage rate	Shrinkage rate	MD	ISO 294-4	0.50-0.70	%
Water absorption rate	23°C,24hr	ASTM D570	0.15	%
	Water absorption rate	23°C,24hr	ISO 62	0.15	%
		Water absorption rate	Equilibrium,23°C,50%RH	ASTM D570	0.32	%
		Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.32	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.