Technical Data Sheet
| thermosetting | Test Condition | Test Method | Test Result |
|---|
| STORAGE STABILITY | | | 7.3 min |
| stripping time | | | 25 min |
| Uncured Properties | Test Condition | Test Method | Test Result |
|---|
| Curing Time | | | 16 hr |
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.13 g/cm³ |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | Shore A | ASTM D2240 | 95to97 |
| Shore hardness | | ASTM D2240 | 48to52 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| compressive strength | | ASTM D695 | 8.27 MPa |
| compressive strength | | ASTM D695 | 11.4 MPa |
| compressive strength | | ASTM D695 | 14.5 MPa |
| compressive strength | | ASTM D695 | 3.45 MPa |
| compressive strength | | ASTM D695 | 5.79 MPa |
| elastomer | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ASTM D412 | 28.3 MPa |
| elongation | Break | ASTM D412 | 350 % |
| tear strength | | ASTM D624 | 87.6 kN/m |
| tear strength | Split | ASTM D470 | 22 kN/m |
| compression set | | ASTM D395B | 32 % |
| Shore hardness | | ASTM D2632 | 42 % |
| tensile strength | | ASTM D412 | 37.9 MPa |
| tensile strength | | ASTM D412 | 15.2 MPa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.