Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | | 1.60 g/cm³ |
| Shrinkage rate | | | 6.0 |
| Shrinkage rate | | | 0.70to0.90 % |
| dimensional stability | | | <0.060 % |
| Water absorption rate | | | 0.35 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | | 24.1to35.9 MPa |
| bending strength | | | 68.9to82.7 MPa |
| compressive strength | | | 124to172 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | | 160 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric constant | | | 3.40 |
| dielectric constant | | | 3.50 |
| dielectric constant | | | 3.50 |
| dielectric constant | | | 3.60 |
| Dissipation Factor | | | 5E-03 |
| Dissipation Factor | | | 6E-03 |
| Dissipation Factor | | | 0.010 |
| Dissipation Factor | | | 0.012 |
| Dissipation Factor | | | 125 sec |
| dielectric strength | | | 62000 V |
| dielectric strength | | | 58000 V |
| Surface Resistivity | | | >1.0E+16 ohms |
| Surface Resistivity | | | 1E+10 ohms |
| Volume resistivity | | | >1.0E+16 ohms·cm |
| Volume resistivity | | | 1E+10 ohms·cm |
| dielectric strength | | | 14 kV/mm |
| dielectric strength | | | 14 kV/mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | | 260 °C |
| Linear coefficient of thermal expansion | | | 4E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.