Technical Data Sheet
| thermosetting | Test Condition | Test Method | Test Result |
|---|
| Thermosetting components | | | 按重量计算的混合比:51 |
| Thermosetting components | Demold Time | | 6.0to8.0 min |
| Thermosetting components | | | 100 |
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | | 0.900to1.20 g/cm³ |
| density | | | 1.010to1.020 g/cm³ |
| density | | | 1.080to1.200 g/cm³ |
| Viscosity | | | 1.00to1.40 Pa·s |
| Viscosity | | | 0.700to1.10 Pa·s |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | Shore A | | 55to65 |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| FOAMING DENSITY | | | 0.900to1.200 g/cm³ |
| PreheatTemperature | | | 50to60 °C |
| PreheatTemperature | | | 50to60 °C |
| PreheatTime | | | 8.0to10.0 hr |
| PreheatTime | | | 8.0to12.0 hr |
| process temperature | | | 40to45 °C |
| process temperature | | | 40to45 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| RossFlex | | | NoCrack |
| WilliamsAbrasion | | | 60.0to100 cc/php |
| elastomer | Test Condition | Test Method | Test Result |
|---|
| tensile strength | Break | | 10.0to14.0 MPa |
| elongation | Break | | 550to650 % |
| tear strength | | | 40.0to55.0 kN/m |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.