PC+AS(SAN)

PC+AS(SAN) T88 GF-30 Covestro - Polycarbonates

Properties:
Filler glass fiber reinforced material 31% filler by weight
Compare

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Suspended wall beam without notch impact strength	23°C	ISO 180	40 kJ/m²
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	-30°C	ISO 180	40 kJ/m²
Impact strength of cantilever beam gap	23°C	ISO 180/A	12 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	-30°C	ISO 180/A	11 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	0.9mm	UL 94	HB

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus	23°C	ISO 527-2/1	10000 MPa
Tensile strain	Break,23°C	ISO 527-2/5	2.0 %
tensile strength	Break,23°C	ISO 527-2/5	135 MPa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	134 °C
Vicat softening temperature	--	ISO 306/B50	132 °C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	126 °C
Linear coefficient of thermal expansion	TD：23to55°C	ISO 11359-2	6E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD：23to55°C	ISO 11359-2	2.5E-05 cm/cm/°C
Vicat softening temperature	--	ISO 306/B120	134 °C

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	Saturation,23°C	ISO 62	0.40 %
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.10 %
Shrinkage rate	MD:260°C,3.00mm	ISO 2577	0.15to0.35 %
Shrinkage rate	Shrinkage rate	TD:260°C,3.00mm	ISO 2577	0.30to0.50 %
density	23°C	ISO 1183	1.38 g/cm³
MeltViscosity	260°C	ISO 11443-A	250 Pa·s

Electrical performance	Test Condition	Test Method	Test Result
Compared to the anti leakage trace index	SolutionA	IEC 60112	PLC 3
Dissipation factor	23°C,1MHz	IEC 60250	8.5E-03
Dissipation factor	Dissipation factor	23°C,100Hz	IEC 60250	3E-03
Relative permittivity	23°C,1MHz	IEC 60250	3.40
Relative permittivity	Relative permittivity	23°C,100Hz	IEC 60250	3.60
Volume resistivity	23°C	IEC 60093	1E+16 ohms·cm
Surface resistivity		IEC 60093	1E+17 ohms
Dielectric strength	23°C,1.00mm	IEC 60243-1	35 kV/mm

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.