PA66 UNITIKA Nylon 66 B2040G33
0
- Properties:Fillerglass fiber reinforced material33%filler by weight
- Usages:Electrical componentsautomotive electronicselectricalelectronic application fields
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ISO 1183 | 1.39 g/cm³ | |
| Shrinkage rate | ISO 294-4 | 0.30 % | |
| ISO 294-4 | 0.80 % | ||
| Water absorption rate | ISO 62 | 1.70 % |
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | ISO 2039-2 | 120 R |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | ISO 527-2 | 170 MPa | |
| elongation at break | ISO 527-2 | 3.0 % | |
| Tensile modulus | ISO 527-2 | 1000 MPa | |
| bending strength | ISO 178 | 260 MPa | |
| Flexural modulus | ISO 178 | 9000 MPa | |
| Charpy Notched Impact Strength | ISO 179/1eA | 10 kJ/m² | |
| Impact strength of simply supported beam without notch | ISO 179/1eU | 75 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Volume resistivity | IEC 60093 | 1E+14 Ω.cm | |
| dielectric strength | IEC 60243-1 | 35 KV/mm | |
| dielectric constant | IEC 60250 | 3.50 1MHz |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Linear coefficient of thermal expansion | ISO 11359-2 | 4E-05 cm/cm／°C | |
| Heat distortion temperature | ISO 75-2/Bf | 250 °C | |
| ISO 75-2/Af | 230 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.