PA612 Zytel® FE3734 NC010 DUPONT USA
107
- Properties:Mineral reinforcementThermal stability
- Usages:Engineering accessoriesAutomotive ApplicationsEngine parts
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.07 | ||
| Shrinkage rate | ASTM D955 | 1.3~1.4 | % | |
| Water absorption rate 23 ℃/24h | ASTM D570/ISO 62 | 1.3 | % | |
| Shrinkage rate | MD：3.20mm | 1.1 | % | |
| TD：3.20mm | 1.1 | % | ||
| TD | ISO294-4 | 1.4 | % | |
| MD | ISO294-4 | 1.3 | % | |
| Water absorption rate | 饱和,23°C,2.00mm | ISO62 | 3.0 | % |
| 平衡,23°C,2.00mm,50%RH | ISO62 | 1.3 | % | |
| Stickiness number | 96%H2SO4 | ISO307 | 95.0 | cm³/g |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | ISO527-2 | 2400 | Mpa | |
| tensile strength | 屈服 | ISO527-2 | 59.0 | Mpa |
| elongation | 屈服 | ISO527-2 | 13 | % |
| Nominal tensile fracture strain | ISO527-2 | 38 | % | |
| Bending modulus | ISO178 | 2200 | Mpa | |
| Impact strength of simply supported beam without notch | -30°C | ISO179/1eU | NoBreak | |
| 23°C | ISO179/1eU | NoBreak | ||
| Rockwell hardness | R级 | ISO2039-2 | 114 | |
| elongation at break | ASTM D412/ISO 527 | 38 | % | |
| Tensile modulus | ASTM D412/ISO 527 | 2400 | kg/cm²(MPa)[Lb/in²] | |
| tensile strength | ASTM D412/ISO 527 | 59 | kg/cm²(MPa)[Lb/in²] | |
| Rockwell hardness | ASTM D785 | R-114 | ||
| Bending modulus | ASTM D790/ISO 178 | 2200 | kg/cm²(MPa)[Lb/in²] | |
| Charpy impact strength | ASTM D256/ISO 179 | 4.8 | kg·cm/cm(J/M)ft·lb/in | |
| ASTM D256/ISO 179 | NB | kg·cm/cm(J/M)ft·lb/in |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | ASTM D648/ISO 75 | 63 | ℃（℉） | |
| melting point | 218 | ℃（℉） | ||
| Hot deformation temperature | 1.8MPa,未退火 | ISO75-2/A | 63.0 | °C |
| Melting temperature | ISO11357-3 | 218 | °C |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Burning rate | 1.00mm | ISO3795 | <100 | mm/min |
| FMVSS flammability | FMVSS302 | B |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.