Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.17 g/cm³ |
| melt mass-flow rate | | ASTM D1238 | 13 g/10min |
| Shrinkage rate | | ASTM D955 | 0.20 % |
| Shrinkage rate | | ASTM D955 | 0.20 % |
| Water absorption rate | | ASTM D570 | 0.13 % |
| Water absorption rate | | ASTM D570 | 0.60 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | R-Scale | ASTM D785 | 105 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ASTM D638 | 6000 MPa |
| tensile strength | | ASTM D638 | 60.0 MPa |
| elongation | Break | ASTM D638 | 5.0 % |
| Flexural modulus | | ASTM D790 | 5500 MPa |
| bending strength | | ASTM D790 | 127 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 78 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC 60093 | 1E+17 ohms |
| Volume resistivity | | IEC 60093 | 1E+18 ohms·cm |
| dielectric strength | | ASTM D149 | 18 kV/mm |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 1 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 112 °C |
| Heat distortion temperature | | ASTM D648 | 105 °C |
| vicat | | ASTM D1525 | 103 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.