ABS 500 TORAY MALAYSIA

Form：Granules | Grade：Injection grade

Properties:

Glass fiber reinforcedHigh impact resistance

Typical Applications:

household electrical appliancesElectronic and electrical components

Supplier(0)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	household electrical appliances \| Electronic and electrical components
Properties:	Glass fiber reinforced \| High impact resistance

Certificates

No Data...

Technical Data Sheet

flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating		UL 94	HB
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
elongation	Break	ISO 527-2/50	>10	%
Bending modulus		ASTM D790	2600	Mpa
bending strength	--3	ASTM D790	82.0	Mpa
bending strength	bending strength	--4	ISO 178	89.0	Mpa
Tensile modulus		ISO 527-2/1	3000	Mpa
tensile strength	Yield2	ASTM D638	55.0	Mpa
tensile strength	tensile strength	Yield	ISO 527-2/50	59.0	Mpa
elongation	Break2	ASTM D638	37	%
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	1.8MPa,Unannealed,6.40mm	ASTM D648	89.0	°C
	Hot deformation temperature	1.8MPa,Unannealed,12.7mm	ASTM D648	94.0	°C
	Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	85.0	°C
Linear coefficient of thermal expansion	MD	ASTM D696	6.9E-05	cm/cm/°C
thermal conductivity		ASTMC177	0.15	W/m/K
Physical properties	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	220°C/10.0kg	ISO 1133	20	g/10min
Shrinkage rate	MD	ASTM D955	0.40-0.60	%
Water absorption rate	23°C,24hr	ASTM D570	0.30	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Dissipation factor	1kHz	ASTM D150	5.6E-03
Surface resistivity		ASTM D257	>1.0E+16	ohms
Volume resistivity	23°C	ASTM D257	>1.0E+16	ohms·cm
Dielectric strength		ASTM D149	22	KV/mm
Dielectric constant	1kHz	ASTM D150	3.10
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	R-Scale	ASTM D785	118

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.