'%20/%3e%3cg%20opacity='1'%20transform='translate(150.5%200)%20rotate(0)'%3e%3cpath%20id='路径%204'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M494%20472.601L487%20410.101L460%20472.601L494%20472.601Z'%3e%3c/path%3e%3cpath%20id='路径%203'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M80%20620.761C152%20676.261%20250%20670.761%20264.5%20670.761C351%20664.261%20412.5%20636.261%20443.5%20620.761C536%20572.261%20580.45%20516.261%20599.5%20492.261C566.05%20492.261%20483.5%20492.261%20465.5%20492.261C408%20532.761%20385.5%20541.761%20369%20550.261C262.5%20599.761%20214%20591.261%20184%20591.261C81%20584.761%2024.3%20510.211%200%20478.261C23%20580.261%2067.5%20609.261%2080%20620.761Z'%3e%3c/path%3e%3cpath%20id='路径%202'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M427.998%202.26C325.498%2014.26%20222.068%2073.64%20247.998%2063.76C384.498%2011.76%20427.998%2024.76%20437.998%2024.76C526.998%2041.76%20559.998%2085.76%20568.998%2095.76C606.498%20142.26%20611.398%20187.06%20613.498%20206.26C631.458%20206.26%20679.498%20206.26%20703.998%20206.26C692.998%20109.26%20633.378%2063.91%20622.998%2056.26C563.998%2012.76%20513.248%205.41%20491.498%202.26C467.498%20-2.24%20437.168%201.19%20427.998%202.26Z'%3e%3c/path%3e%3cpath%20id='路径%201'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M232%20206.763C243%20178.763%20262%20156.763%20273.5%20140.263C329%2080.2634%20374%2069.7634%20410.5%2061.2634C446.5%2052.2634%20499%2061.2634%20504.5%2061.2634C446%2039.7634%20393%2040.7634%20387.5%2040.7634C308.5%2047.2634%20259.5%2075.2634%20237%2088.7634C162.5%20135.263%20122.95%20185.313%20106%20206.763C139.86%20206.763%20221.5%20206.763%20232%20206.763Z'%3e%3c/path%3e%3c/g%3e%3cpath%20id='减去顶层'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M379.519,227.698l4.237,4.101l-38.576,198.188h98.804l3.966,3.839l-7.614,38.817h-147.091l-4.064,-3.934l46.975,-241.011zM900.883,363.706c-21,-8.75%20-34.89067,-17.22667%20-41.672,-25.43c-6.78133,-8.20333%20-10.172,-19.19533%20-10.172,-32.976c0,-24.06267%208.832,-43.75033%2026.496,-59.063c17.664,-15.312%2040.55067,-22.968%2068.66,-22.968c11.266,0%2022.231,1.121%2032.895,3.363c10.664,2.242%2020.974,5.60533%2030.93,10.09l-8.139,40.672l-5.05,2.827c-6.54467,-5.18467%20-13.96233,-9.21167%20-22.253,-12.081c-9.95333,-3.44533%20-21.00033,-5.168%20-33.141,-5.168c-12.906,0%20-23.406,3.08967%20-31.5,9.269c-8.09333,6.18%20-12.14,14.08233%20-12.14,23.707c0,9.18733%2010.06233,18.32%2030.187,27.398l1.149,0.493l19.031,8.367c15.96867,7.10933%2027.64433,15.668%2035.027,25.676c7.38267,10.00733%2011.074,22.28467%2011.074,36.832c0,25.156%20-8.80467,45.226%20-26.414,60.21c-17.60933,14.98467%20-41.39833,22.477%20-71.367,22.477c-12.03133,0%20-24.30867,-1.422%20-36.832,-4.266c-12.52333,-2.84333%20-25.56633,-7.16367%20-39.129,-12.961l8.62,-44.559l4.63,-2.592c9.52333,7.45333%2019.435,13.24467%2029.735,17.374c11.59333,4.64867%2023.24167,6.973%2034.945,6.973c14.54667,0%2025.97633,-3.19933%2034.289,-9.598c8.31267,-6.39867%2012.469,-15.06667%2012.469,-26.004c0,-6.78133%20-1.914,-12.66%20-5.742,-17.636c-3.82867,-4.97667%20-9.51633,-9.051%20-17.063,-12.223zM54.3672,227.698h68.9058c25.81267,0%2045.473,5.004%2058.981,15.012c13.50733,10.008%2020.261,24.58233%2020.261,43.723c0,12.46867%20-1.996,24.82767%20-5.988,37.077c-3.992,12.25%20-9.16,21.98467%20-15.504,29.204c-8.53133,9.95267%20-19.14067,17.14433%20-31.828,21.575c-12.68733,4.42867%20-29.14817,6.643%20-49.3825,6.643h-26.9063l-17.8828,91.711h-43.7778l-3.88732,-3.761zM642.062,227.698h59.063l18.238,240.969l-4.109,3.976h-43.66l-2.297,-60.539h-0.041l-1.756,-40.844l-0.04,-0.002l-3.249,-98.607l-41.151,94.615l-0.06,-0.006l-20.5,47.5h0.005l-25.411,57.883h-43.849l-3.589,-3.474zM94.7266,268.386l-13.7813,71.859h23.4607c15.96867,0%2027.918,-3.69133%2035.848,-11.074c7.92933,-7.38267%2011.894,-18.457%2011.894,-33.223c0,-9.95333%20-2.84367,-17.03533%20-8.531,-21.246c-5.68733,-4.21067%20-15.367,-6.316%20-29.039,-6.316z'%3e%3c/path%3e%3c/svg%3e)
PC 4701R-110001 SABIC INNOVATIVE US
112
Form：Granules | Grade：Injection grade
Properties:
High temperature resistantransparent
Typical Applications:
Electronic and electrical components
Product Description
Certificates(0)
Datasheet
Product Description
| Typical Applications: | Electronic and electrical components |
| Properties: | High temperature resistan | transparent |
Certificates
No Data...
Technical Data Sheet
| optical performance | Test Condition | Test Method | Test Result | Test Unit |
|---|---|---|---|---|
| Refractive index | ASTM D542 | 1.600 | ||
| transmissivity | 2540 μm | ASTM D1003 | 85.0 | % |
| turbidity | 2540 μm | ASTM D1003 | 1.0 | % |
| impact performance | Test Condition | Test Method | Test Result | Test Unit |
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 无断裂 | |
| -30°C | ISO 180/1U | 无断裂 | ||
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 35 | kJ/m² |
| -30°C | ISO 180/1A | 11 | kJ/m² | |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 无断裂 | |
| -30°C | ISO 179/1eU | 无断裂 | ||
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 46 | kJ/m² |
| -30°C | ISO 179/1eA | 13 | kJ/m² | |
| Suspended wall beam without notch impact strength | 23°C | ASTM D4812 | 3200 | J/m |
| Dart impact | 23°C | ASTM D3029 | 149 | J |
| Impact strength of cantilever beam gap | ASTM D1822 | 577 | kJ/m² | |
| flammability | Test Condition | Test Method | Test Result | Test Unit |
| Burning wire flammability index | 2.0 mm | IEC 60695-2-12 | 850 | °C |
| mechanical properties | Test Condition | Test Method | Test Result | Test Unit |
| Bending modulus | ISO 178 | 2300 | Mpa | |
| Tensile strain | Break | ISO 527-2/50 | > 50 | % |
| Yield | ISO 527-2/50 | 7.0 | % | |
| tensile strength | Yield | ISO 527-2/50 | 70.0 | Mpa |
| Tensile modulus | ISO 527-2/1 | 2300 | Mpa | |
| tensile strength | Yield | ASTM D638 | 65.0 | Mpa |
| Break | ASTM D638 | 77.0 | Mpa | |
| elongation | Break | ASTM D638 | 78 | % |
| Bending modulus | 50.0 mm Span | ASTM D790 | 2330 | Mpa |
| bending strength | Yield, 50.0 mm Span | ASTM D790 | 97.0 | Mpa |
| injection | Test Condition | Test Method | Test Result | Test Unit |
| drying temperature | 125 to 135 | °C | ||
| Hopper temperature | 60 to 80 | °C | ||
| Temperature at the rear of the barrel | 300 to 320 | °C | ||
| Temperature in the middle of the barrel | 310 to 330 | °C | ||
| Temperature at the front of the material cylinder | 320 to 340 | °C | ||
| Spray nozzle temperature | 320 to 340 | °C | ||
| Processing (melt) temperature | 325 to 360 | °C | ||
| Mold temperature | 100 to 125 | °C | ||
| Exhaust hole depth | 0.025 to 0.076 | mm | ||
| Mold temperature | 80 to 115 | °C | ||
| Back pressure | 0.300 to 0.700 | Mpa | ||
| Screw speed | 40 to 70 | rpm | ||
| drying temperature | 120 | °C | ||
| drying time | 3.0 to 4.0 | hr | ||
| Suggested maximum moisture content | 0.020 | % | ||
| Suggested injection volume | 40 to 60 | % | ||
| Temperature at the rear of the barrel | 325 to 350 | °C | ||
| Temperature in the middle of the barrel | 340 to 360 | °C | ||
| Temperature at the front of the material cylinder | 350 to 370 | °C | ||
| Spray nozzle temperature | 345 to 365 | °C | ||
| Processing (melt) temperature | 350 to 370 | °C | ||
| thermal performance | Test Condition | Test Method | Test Result | Test Unit |
| thermal conductivity | ISO 8302 | 0.21 | W/m/K | |
| Linear coefficient of thermal expansion | 23 to 80°C，Flow | ISO 11359-2 | 8.0E-5 | cm/cm/°C |
| Ball Pressure Test | 123 to 127°C | IEC 60695-10-2 | 通过 | |
| Vicat softening temperature | -- | ISO 306/B120 | 170 | °C |
| -- | ISO 306/B50 | 175 | °C | |
| -- | ISO 306/A50 | 185 | °C | |
| Hot deformation temperature | 1.8 MPa, Unannealed, 4.00 mm, 100 mm Span | ISO 75-2/Ae | 150 | °C |
| 0.45 MPa, Unannealed, 4.00 mm, 100 mm Span | ISO 75-2/Be | 165 | °C | |
| thermal conductivity | ASTM C177 | 0.21 | W/m/K | |
| RTI Elec | UL 746 | 130 | °C | |
| RTI Imp | UL 746 | 130 | °C | |
| RTI | UL 746 | 130 | °C | |
| Hot deformation temperature | 1.8 MPa, Unannealed, 3.20 mm | ASTM D648 | 148 | °C |
| Linear coefficient of thermal expansion | -40 to 95°C，Flow | ASTM E831 | 8.1E-5 | cm/cm/°C |
| specific heat | ASTM C351 | 1260 | J/kg/°C | |
| Physical properties | Test Condition | Test Method | Test Result | Test Unit |
| Shrinkage rate | Flow | Internal Method | 0.90 | % |
| Melt Volume Flow Rate (MVR) | 300°C/5.0 kg | ISO 1133 | 6.00 | cm3/10min |
| Specific volume | ASTM D792 | 0.830 | cm³/g | |
| melt mass-flow rate | 300°C/1.2 kg | ASTM D1238 | 2.0 | g/10 min |
| 300°C/6.1 kg | ASTM D1238 | 9.0 | g/10 min | |
| Shrinkage rate | 3.20 mm，Flow | Internal Method | 0.80 - 1.0 | % |
| Water absorption rate | 24 hr | ASTM D570 | 0.19 | % |
| Electrical performance | Test Condition | Test Method | Test Result | Test Unit |
| Relative permittivity | 1 MHz | IEC 60250 | 3.10 | |
| Dissipation factor | 100 Hz | IEC 60250 | 0.026 | |
| Volume resistivity | ASTM D257 | > 2.5E+17 | ohms·cm | |
| Dielectric strength | 3.20 mm, in Air | ASTM D149 | 20 | KV/mm |
| Dielectric constant | 60 Hz | ASTM D150 | 3.27 | |
| 1 MHz | ASTM D150 | 3.10 | ||
| Dissipation factor | 50 Hz | ASTM D150 | 1.6E-3 | |
| 60 Hz | ASTM D150 | 1.6E-3 | ||
| Dielectric constant | 50 kHz | ASTM D150 | 3.27 | |
| Dissipation factor | 100 Hz | ASTM D150 | 0.026 | |
| Arc resistance | ASTM D495 | PLC 6 | ||
| Compared to the anti leakage trace index | UL 746 | PLC 3 | ||
| High arc combustion index | UL 746 | PLC 3 | ||
| High voltage arc tracing rate | UL 746 | PLC 3 | ||
| Hot wire ignition | UL 746 | PLC 2 | ||
| hardness | Test Condition | Test Method | Test Result | Test Unit |
| Rockwell hardness | R -Sale | ISO 2039-2 | 127 | |
| M-Scale | ASTM D785 | 92 | ||
| R-Scale | ASTM D785 | 127 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.