Polyester Alloy Generic Polyester Alloy - GlassInorganic Generic
0
- Properties:Fillerglass inorganic
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Apparent density | ISO 60 | 0.75to0.88 g/cm³ | |
| Shrinkage rate | ISO 294-4 | 0.025to0.56 % | |
| density | ISO 1183 | 2.00to2.10 g/cm³ |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Flexural modulus | ISO 178 | 13500to17100 MPa | |
| bending strength | ISO 178 | 90.0to150 MPa | |
| tensile strength | ISO 527-2 | 50.0to65.0 MPa | |
| compression stress | ISO 604 | 173to175 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | 3.0to5.5 kJ/m² | |
| Impact strength of simply supported beam without notch | ISO 179 | 7.4to17 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 0 | |
| Surface Resistivity | IEC 60093 | 5.5E+12到5.5E+14 ohms | |
| Volume resistivity | IEC 60093 | 5.5E+13到6.0E+14 ohms·cm | |
| dielectric strength | IEC 60243-1 | 23 kV/mm | |
| Dissipation Factor | IEC 60250 | 0.015to0.050 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ISO 75-2/B | 200to250 °C | |
| ISO 75-2/A | 198to250 °C | ||
| ISO 75-2/C | 110to220 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.