Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Water absorption rate | | % | 0.080to2.9 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| compressive strength | | | 20.69to237.24 Mpa |
| elongation | | % | 4.0to8.0 |
| bending strength | | | 58.62to253.79 Mpa |
| Flexural modulus | | | 2551.72to3220.69 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | J/m | 0.006to0.026 |
| film | Test Condition | Test Method | Test Result |
|---|
| tensile strength | Break | | 191.72to241.38 Mpa |
| Elmendorf tear strength | | g | 6.8to38 |
| elongation | Break | % | 72to95 |
| film thickness | | mil | 0.95to3.1 |
| Secant modulus | | | 2793.1to3172.41 Mpa |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric strength | | V/mil | 390to7800 |
| dielectric constant | | | 2.95to3.45 |
| Volume resistivity | | ohms·cm | 4.0E+12到5.8E+15 |
| Dissipation Factor | | | 8.0E-4到2.1E-3 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| RTI Elec | | °C | 130to240 |
| Linear coefficient of thermal expansion | | mm/mm/°C | 38.1E-5到50.8E-5 |
| RTI | | °C | 130to210 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.