ABS T4060
0
- Usages:Automotive internal parts and equipment
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ISO1183 | 1.06 g/cm³ | |
| melt mass-flow rate | ISO1133 | 9.0 g/10min | |
| Shrinkage rate | ISO294-4 | 0.40到0.70 % | |
| Water absorption rate | ISO62 | 1.0 % | |
| ISO62 | 0.22 % |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL94 | HB | |
| UL94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile strain | ISO527-2 | 3.6 % | |
| ISO527-2 | 2.4 % | ||
| Break | ISO527-2 | 12 % | |
| Bending stress | ISO178 | 70.0 MPa | |
| Tensile modulus | ISO527-2/1 | 2400 MPa | |
| Tensile stress | Yield | ISO527-2/50 | 51.0 MPa |
| ISO527-2 | 63.0 MPa | ||
| ISO527-2 | 19.0 MPa | ||
| Tensile strain | Yield | ISO527-2/50 | 2.6 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO179/1eA | 14 kJ/m² | |
| Impact strength of simply supported beam without notch | ISO179/1eU | 无断裂 | |
| Impact strength of cantilever beam gap | ISO180/1A | 15 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | ISO75-2/Be | 111 °C | |
| ISO75-2/Ae | 106 °C | ||
| vicat | ISO306/B50 | 106 °C | |
| Linear thermal expansion coefficient | ISO11359-2 | 9.5E-04 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.