Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Water absorption rate | | ISO62 | 0.20 % |
| density | | ASTMD792 | 1.23 g/cm³ |
| melt mass-flow rate | | ASTMD1238 | 18 g/10min |
| Shrinkage rate | | ASTMD955 | 0.40到0.80 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | R-Scale | ASTMD785 | 118 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | HB |
| UL flame retardant rating | | UL94 | HB |
| Hot filament ignition temperature | | IEC60695-2-13 | 650 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | Break | ASTMD638 | 70.0 MPa |
| elongation | Break | ASTMD638 | 3.0 % |
| Flexural modulus | | ASTMD790 | 5000 MPa |
| bending strength | Break | ASTMD790 | 100 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTMD256 | 50 J/m |
| Impact strength of cantilever beam gap | | ASTMD256 | 70 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| | IEC60250 | 2.90 |
| Dissipation Factor | | IEC60250 | 0.050 |
| Surface Resistivity | | IEC60093 | 1E+15 ohms |
| Volume resistivity | | IEC60093 | 1E+15 ohms·cm |
| dielectric strength | | IEC60243-1 | 25 kV/mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ASTMD648 | 115 °C |
| vicat | | ASTMD15254 | 123 °C |
| | ISO11359-2 | 4E-06 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare