PA66/PTFE LNP™ LUBRICOMP™ RL-4020 SABIC INNOVATIVE US
92
- Properties:High temperature resistanresist fatigue
- Usages:Electronic and electrical accessoriesAutomotive componentsCasters
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shrinkage rate | ASTMD955 | 2.2 % | |
| ASTMD955 | 2.6 % | ||
| ISO294-4 | 2.6 % | ||
| ISO294-4 | 2.2 % | ||
| Water absorption rate | ASTMD570 | 0.94 % | |
| ISO62 | 1.2 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Suspended wall beam without notch impact strength | ASTMD4812 | 900 J/m | |
| ISO180/1U | 59 kJ/m² | ||
| Dart impact equipped with measuring instruments | ASTMD3763 | 3.59 J | |
| ISO6603-2 | 4.20 J |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| elongation | ASTMD638 | 14 % | |
| ISO527-2 | 18 % | ||
| Flexural modulus | ASTMD790 | 3040 Mpa | |
| ISO178 | 2840 Mpa | ||
| bending strength | ASTMD790 | 112 Mpa | |
| ISO178 | 89.4 Mpa | ||
| ASTMD3702Modified | 0.27 | ||
| ASTMD3702Modified | 0.23 | ||
| Wear factor - Washer | ASTMD3702Modified | 49.0 10^-10in^5-min/ft-lb-hr | |
| Tensile modulus | ASTMD638 | 3090 Mpa | |
| ISO527-2/1 | 3180 Mpa | ||
| tensile strength | ASTMD638 | 75.1 Mpa | |
| ISO527-2 | 73.0 Mpa | ||
| ASTMD638 | 74.7 Mpa | ||
| ISO527-2 | 73.0 Mpa | ||
| elongation | ASTMD638 | 14 % | |
| ISO527-2 | 17 % |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ASTMD648 | 76.1 °C | ||
| ISO75-2/Af | 74.0 °C | ||
| ASTME831,ISO11359-2 | 8.3E-05 cm/cm/°C | ||
| ASTME831,ISO11359-2 | 8.6E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.