Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTMD792 | 1.41 g/cm³ |
| melt mass-flow rate | | ASTMD1238 | 45 g/10min |
| Shrinkage rate | | ASTMD955 | 1.8to2.1 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | M-Scale | ASTMD785 | 82 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | HB |
| UL flame retardant rating | | UL94 | HB |
| UL flame retardant rating | | UL94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | Yield | ASTMD638 | 62.7 MPa |
| elongation | Break | ASTMD638 | 50 % |
| Flexural modulus | | ASTMD790 | 2660 MPa |
| bending strength | Yield | ASTMD790 | 93.8 MPa |
| Itself - Dynamic | ASTMD1894 | 0.16 |
| Itself - Static | ASTMD1894 | 0.12 |
| | ASTMD1044 | 14.0 mg |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTMD256 | 54 J/m |
| Impact strength of cantilever beam gap | | ASTMD256 | 640 J/m |
| ReverseNotchIzodImpact | | ASTMD256 | 650 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| High arc combustion index (HAI) | | UL746 | PLC 0 |
| High arc combustion index (HAI) | | UL746 | PLC 0 |
| High Voltage Arc Traceability Rate (HVTR) | | UL746 | PLC 0 |
| Surface Resistivity | | ASTMD257 | 1E+14 ohms |
| Volume resistivity | | ASTMD257 | 1E+16 ohms·cm |
| Hot wire ignition (HWI) | | UL746 | PLC 5 |
| Hot wire ignition (HWI) | | UL746 | PLC 4 |
| dielectric strength | | ASTMD149 | 24 kV/mm |
| dielectric constant | | ASTMD150 | 3.80 |
| Dissipation Factor | | ASTMD150 | 7E-03 |
| arc resistance | | ASTMD495 | PLC 5 |
| Compared to the Leakage Tracking Index (CTI) | | UL746 | PLC 0 |
| High arc combustion index (HAI) | | UL746 | PLC 0 |
| Hot wire ignition (HWI) | | UL746 | PLC 5 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| RTI Str | | UL746 | 95.0 °C |
| RTI Str | | UL746 | 100 °C |
| RTI Elec | | UL746 | 110 °C |
| RTI Elec | | UL746 | 110 °C |
| RTI Imp | | UL746 | 95.0 °C |
| RTI Imp | | UL746 | 95.0 °C |
| RTI Imp | | UL746 | 95.0 °C |
| RTI Str | | UL746 | 90.0 °C |
| Heat distortion temperature | | ASTMD648 | 160 °C |
| Heat distortion temperature | | ASTMD648 | 110 °C |
| | ASTMD696 | 1E-04 cm/cm/°C |
| RTI Elec | | UL746 | 110 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.