Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183 | 1.16 g/cm³ |
| Melt volume flow rate | | ISO1133 | 32.0 cm³/10min |
| Water absorption rate | | ISO62 | 7.0 % |
| Water absorption rate | | ISO62 | 0.40 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| | ISO868 | 33 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | IEC60695-11-10,-20 | HB |
| UL flame retardant rating | | IEC60695-11-10,-20 | HB |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ISO180/1A | NoBreak |
| Charpy Notched Impact Strength | | ISO179/1eA | NoBreak |
| Charpy Notched Impact Strength | | ISO179/1eA | NoBreak |
| Impact strength of cantilever beam gap | | ISO180/1A | NoBreak |
| Impact strength of cantilever beam gap | | ISO180/1A | NoBreak |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO527-2 | 45.0 MPa |
| Tensile stress | Break | ISO527-2 | 14.0 MPa |
| Tensile stress | | ISO527-2 | 2.50 MPa |
| Tensile stress | | ISO527-2 | 4.00 MPa |
| Tensile stress | | ISO527-2 | 7.00 MPa |
| Tensile stress | | ISO527-2 | 8.50 MPa |
| Nominal tensile fracture strain | | ISO527-2 | 450 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| CTI | | IEC60112 | 600 V |
| Volume resistivity | | IEC60093 | 1E+14 ohms·cm |
| dielectric strength | | IEC60243-1 | 20 kV/mm |
| | IEC60250 | 4.70 |
| | IEC60250 | 4.40 |
| Dissipation Factor | | IEC60250 | 0.031 |
| Dissipation Factor | | IEC60250 | 0.081 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO11359-2 | 1.5E-04 cm/cm/°C |
| melting temperature | | ISO11357-3 | 212 °C |
| | ISO11359-2 | 1.5E-04 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.