| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | | 1.05 g/cm³ |
| density | | | 1.07 g/cm³ |
| density | Base Resin | | 1.20 g/cm³ |
| Shrinkage rate | | ASTM D2566 | 0.10to0.50 % |
| thermosetting | Test Condition | Test Method | Test Result |
|---|
| Thermosetting components | Resin | | 按重量计算的混合比:100按容量计算的混合比:100 |
| Thermosetting components | Hardener | | 按重量计算的混合比:89按容量计算的混合比:100 |
| Thermosetting components | Demold Time | | 10to20 min |
| Cured Properties | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | ASTM D2240 | 75to85 |
| Tensile modulus | | ASTM D638 | 1720 MPa |
| tensile strength | | ASTM D638 | 44.8 MPa |
| elongation | Break | ASTM D638 | 5.0 % |
| Uncured Properties | Test Condition | Test Method | Test Result |
|---|
| Viscosity | | | 0.50 Pa·s |
| Viscosity | | | 0.90 Pa·s |
| Viscosity | | | 1.0 Pa·s |
| Viscosity | | | 40 hr |
| Viscosity | | | 0.83to1.2 min |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Flexural modulus | | ASTM D790 | 1140 MPa |
| bending strength | | ASTM D790 | 51.7 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 140 J/m |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 65.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.