Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.30 g/cm³ |
| melt mass-flow rate | | ASTM D1238 | 19 g/10min |
| Melt volume flow rate | | ISO 1133 | 17.0 cm3/10min |
| Shrinkage rate | | 内部方法 | 1.2-1.4 % |
| Shrinkage rate | | 内部方法 | 1.2-1.4 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-0 |
| UL flame retardant rating | | UL 94 | 5VA |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ASTM D638 | 1970 Mpa |
| tensile strength | | ASTM D638 | 49.0 Mpa |
| tensile strength | | ASTM D638 | 39.3 Mpa |
| elongation | | ASTM D638 | 6.0 % |
| elongation | | ASTM D638 | 50 % |
| Flexural modulus | | ASTM D790 | 2000 Mpa |
| bending strength | | ASTM D790 | 78.6 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 670 J/m |
| Dart impact | | ASTM D3763 | 49.7 J |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| High Voltage Arc Traceability Rate (HVTR) | | UL 746 | PLC 4 |
| Hot wire ignition (HWI) | | UL 746 | PLC 2 |
| arc resistance | | ASTM D495 | PLC6 |
| Compared to the Leakage Tracking Index (CTI) | | UL 746 | PLC 2 |
| High arc combustion index (HAI) | | UL 746 | PLC 0 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 127 °C |
| Heat distortion temperature | | ASTM D648 | 85.0 °C |
| vicat | | ASTM D15255 | 135 °C |
| Linear coefficient of thermal expansion | | ASTME831 | 7.9E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | | ASTME831 | 8.6E-05 cm/cm/°C |
| RTI Elec | | UL 746 | 100 °C |
| RTI Imp | | UL 746 | 85.0 °C |
| RTI Str | | UL 746 | 100 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.