Technical Data Sheet
| Uncured Properties | Test Condition | Test Method | Test Result |
|---|
| Color | | | Clear/Transparent |
| Color | | | Grey |
| density | | | 0.918 g/cm³ |
| density | | | 2.27 g/cm³ |
| density | | | 1.4to2.2 Pa·s |
| density | | | >2.0 hr |
| density | Pot Life | | 210 min |
| physical property | Test Condition | Test Method | Test Result |
|---|
| Particle size | | | <50.0 µm |
| Cured Properties | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | | 91 |
| LapShearStrength | | | >13.3 MPa |
| relative permittivity | | | 5.69 |
| Volume resistivity | | | >2.0E+13 ohms·cm |
| Dissipation Factor | | | 9E-03 |
| thermosetting | Test Condition | Test Method | Test Result |
|---|
| Thermosetting components | | | 按重量计算的混合比:10 |
| Thermosetting components | | | 按重量计算的混合比:1.0 |
| Thermosetting components | | | 52 wk |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| operate temperature | | | -55-150 °C |
| operate temperature | | | -55-250 °C |
| operate temperature | | | 5.44 GPa |
| operate temperature | | | 2.20 |
| weight loss on heating | | | 0.40 % |
| weight loss on heating | | | 0.66 % |
| weight loss on heating | | | 1.8 % |
| DegradationTemperature | | TGA | 314 °C |
| Shear Strength | | | 23.4 MPa |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Glass Transition Temperature | | | >40.0 °C |
| Linear coefficient of thermal expansion | | | 3.1E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | | | 1.4E-04 cm/cm/°C |
| Linear coefficient of thermal expansion | | | 1.0 W/m/K |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.