Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183 | 1.38 g/cm³ |
| melt mass-flow rate | | ISO1133 | 10 g/10min |
| Melt volume flow rate | | ISO1133 | 9.00 cm3/10min |
| Shrinkage rate | | ISO294-4 | 1.7 % |
| Shrinkage rate | | ISO294-4 | 1.9 % |
| Water absorption rate | | ISO62 | 0.70 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ISO2039-2 | 65 |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| ColorNumber | | | CF2003/CF2004 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Bending stress | | ISO178 | 60.0 Mpa |
| | JISK7218 | 0.60 |
| | JISK7218 | 0.30 |
| Wear factor | | JISK7218 | <1.0 10^-8mm³/N·m |
| Wear factor | | JISK7218 | 100 10^-8mm³/N·m |
| Wear factor | | JISK7218 | 600 10^-8mm³/N·m |
| Wear factor | | JISK7218 | 700 10^-8mm³/N·m |
| Tensile modulus | | ISO527-2 | 1850 Mpa |
| Tensile stress | | ISO527-2 | 46.0 Mpa |
| Nominal tensile fracture strain | | ISO527-2 | 55 % |
| Flexural modulus | | ISO178 | 1700 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO179/1eA | 12 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC60093 | 7E+12 ohms |
| Volume resistivity | | IEC60093 | 1E+13 ohms·cm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/A | 82.0 °C |
| | 内部方法 | 1.3E-04 cm/cm/°C |
| | 内部方法 | 1.3E-04 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.