PA66 TSG-30/4 V0 EMS-CHEMIE SWITZERLAND

Form：Granules | Grade：Flame retardant grade

Properties:

Thermal stabilityGlass fiber reinforced

Typical Applications:

Automotive Applications

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Automotive Applications
Properties:	Thermal stability \| Glass fiber reinforced

Certificates

No Data...

Technical Data Sheet

Other performance	Test Condition	Test Method	Test Result	Test Unit
Flammability level		UL 94	干燥｜V-0
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Ball Pressure Test		ISO 2039-1	干燥｜255	Mpa
Ball Pressure Test	Ball Pressure Test		ISO 2039-1	调节后｜130	Mpa
Tensile modulus		ISO 527-2	干燥｜10500	Mpa
Tensile modulus	Tensile modulus		ISO 527-2	调节后｜6500	Mpa
tensile strength	Break	ISO 527-2	干燥｜150	Mpa
tensile strength	tensile strength	Break	ISO 527-2	调节后｜90.0	Mpa
Tensile strain	Break	ISO 527-2	干燥｜2.5	%
Tensile strain	Tensile strain	Break	ISO 527-2	调节后｜4.5	%
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	干燥｜9.0	kJ/m²
	Charpy Notched Impact Strength	-30°C	ISO 179/1eA	调节后｜8.5	kJ/m²
		Charpy Notched Impact Strength	23°C	ISO 179/1eA	干燥｜9.5	kJ/m²
		Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	调节后｜14	kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	干燥｜60	kJ/m²
	Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	调节后｜60	kJ/m²
		Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	干燥｜65	kJ/m²
		Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	调节后｜70	kJ/m²
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/A	干燥｜235	°C
Hot deformation temperature	Hot deformation temperature	8.0 MPa, Unannealed	ISO 75-2/C	干燥｜165	°C
Continuous use temperature	--3	ISO 2578	干燥｜100 -120	°C
Continuous use temperature	Continuous use temperature	--4	Internal Method	干燥｜220	°C
Melting temperature		ISO 11357-3	干燥｜260	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate	TD	ISO 294-4	干燥｜0.70	%
Shrinkage rate	Shrinkage rate	MD	ISO 294-4	干燥｜0.20	%
Water absorption rate	Saturation, 23°C	ISO 62	干燥｜4.0	%
Water absorption rate	Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	干燥｜1.5	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Volume resistivity		IEC 60093	调节后｜1.0E+12	ohms·cm
Dielectric strength		IEC 60243-1	干燥｜28	KV/mm
Dielectric strength	Dielectric strength		IEC 60243-1	调节后｜26	KV/mm
Compared to the anti leakage trace index		IEC 60112		V
Surface resistivity		IEC 60093	调节后｜1.0E+10	ohms
Volume resistivity		IEC 60093	干燥｜1.0E+12	ohms·cm

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.