PA6 B3WG6 BK BASF MALAYSIA

Form：Granules | Grade：Enhanced level

Properties:

Thermal stabilityOil resistantFiller: Glass fiber reinf30%Filler by weight30% filler by weight

Typical Applications:

Automotive sectorEngine hood partsApplication in the automotive field

Supplier(1)

Product Description

Certificates(1)

Datasheet

Product Description

Typical Applications:	Automotive sector \| Engine hood parts \| Application in the automotive field
Properties:	Thermal stability \| Oil resistant \| Filler: Glass fiber reinf \| 30% \| Filler by weight \| 30% filler by weight

Certificates

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Charpy Notched Impact Strength	-30°C	ISO 179	9.0	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179	12	kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179	65	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179	80	kJ/m²
Impact strength of cantilever beam gap	-40°C	ASTM D256	110	J/m
	Impact strength of cantilever beam gap	23°C	ASTM D256	150	J/m
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180	12	kJ/m²
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus	23°C	ISO 527-2	9500	Mpa
tensile strength	Break,23°C	ASTM D638	180	Mpa
tensile strength	tensile strength	Break,23°C	ISO 527-2	180	Mpa
Tensile strain	Break,23°C	ISO 527-2	3.0	%
Bending modulus	23°C	ISO 178	8300	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45MPa,Unannealed	ASTM D648	220	°C
	Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	220	°C
		Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	210	°C
		Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	205	°C
Melting temperature		ASTM D3418	220	°C
Melting temperature	Melting temperature		ISO 3146	220	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density		ASTM D792	1.36	g/cm³
density	density		ISO 1183	1.36	g/cm³
Melt Volume Flow Rate (MVR)	275°C/5.0kg	ISO 1133	40.0	cm3/10min
Shrinkage rate	MD：3.18mm		0.30	%
Water absorption rate	Saturation	ASTM D570	6.6	%
	Water absorption rate	Saturation,23°C	ISO 62	6.6	%
		Water absorption rate	Equilibrium,50%RH	ASTM D570	2.1	%
		Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	2.1	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.