PA6 TSGZ-15 NA EMS-CHEMIE TAIWAN

Form：Granules | Grade：Injection grade

Properties:

Glass fiber reinforcedThermal stabilityFiller: Glass fiber reinf15% filler by weight

Typical Applications:

Automotive Applicationssporting goodsLaptop caseConsumer product application fieldPower/Other ToolsHousehold goodsApplication in the automotive fieldAutomotive interior partsHome appliance componentsElectrical/Electronic ApplicationsEngineering accessoriesIndustrial applications

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Automotive Applications \| sporting goods \| Laptop case \| Consumer product application field \| Power/Other Tools \| Household goods \| Application in the automotive field \| Automotive interior parts \| Home appliance components \| Electrical/Electronic Applications \| Engineering accessories \| Industrial applications
Properties:	Glass fiber reinforced \| Thermal stability \| Filler: Glass fiber reinf \| 15% filler by weight

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	-30°C	kJ/m²	60
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	kJ/m²	75
flammability	Test Condition	Test Method	Test Result	Test Unit
Flammability level	0.8mm		HB	--
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus		MPa	5600	2900
tensile strength	Break	MPa	110	65.0
Tensile strain	Break	%	4.0
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Continuous use temperature	--3	°C	200	--
Melting temperature		°C	260	--
Linear coefficient of thermal expansion	MD	cm/cm/°C	2E-05	--
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD	cm/cm/°C	1.1E-04	--
Hot deformation temperature	1.8MPa,Unannealed	°C	215	--
Hot deformation temperature	Hot deformation temperature	8.0MPa,Unannealed	°C	60.0	--
Continuous use temperature	--2	°C	100to120	--
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate	TD	%	0.70	--
Shrinkage rate	Shrinkage rate	MD	%	0.10	--
Water absorption rate	Saturation,23°C	%	8.0	--
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	%	3.0	--
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Surface resistivity		ohms	--	1E+10
Volume resistivity		ohms·cm	1E+13
Dielectric strength		kV/mm	30	27
hardness	Test Condition	Test Method	Test Result	Test Unit
Ball Pressure Test		MPa	160	75.0

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.