| thermosetting | Test Condition | Test Method | Test Result |
|---|
| Resin | | 按重量计算的混合比:100 |
| Hardener | | 按重量计算的混合比:22 |
| Uncured Properties | Test Condition | Test Method | Test Result |
|---|
| STORAGE STABILITY | | | 7.0到9.0 min |
| density | | | 1.03到1.07 g/cm³ |
| | | 25到35 Pa·s |
| Curing Time | | | 4.0到5.0 hr |
| hardness | Test Condition | Test Method | Test Result |
|---|
| | ISO7619 | 73到77 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO179 | 1.8到2.2 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Flexural modulus | | ISO178 | 2300到2800 MPa |
| Bending stress | | ISO178 | 18.0到22.0 MPa |
| compression stress | | ISO604 | 29.0到35.0 MPa |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| MartensTemperature | | DIN53458 | 54到58 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.