ABS TR-530F LG CHEM KOREA

Form：Granules | Grade：Transparent level

Properties:

heat-resisting

Typical Applications:

Automotive Applications

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Automotive Applications
Properties:	heat-resisting

Certificates

No Data...

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result	Test Unit
transmissivity		ASTM D1003	89.0	%
turbidity		ASTM D1003	3.0	%
impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of cantilever beam gap	-30°C, 3.20 mm, Injection	ASTM D256	240	J/m
	Impact strength of cantilever beam gap	-30°C, 6.40 mm, Injection	ASTM D256	90	J/m
		Impact strength of cantilever beam gap	23°C, 3.20 mm, Injection	ASTM D256	90	J/m
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C, 6.40 mm, Injection	ASTM D256	240	J/m
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus	23°C, 3.20 mm, Injection	ASTM D638	1350	Mpa
tensile strength	Yield, 23°C, 3.20 mm, Injection	ASTM D638	33.0	Mpa
elongation	Break, 23°C, 3.20 mm, Injection	ASTM D638	> 15	%
Bending modulus	23°C, 3.20 mm, Injection	ASTM D790	1500	Mpa
bending strength	23°C, 3.20 mm, Injection	ASTM D790	49.0	Mpa
injection	Test Condition	Test Method	Test Result	Test Unit
drying temperature			80 to 90	°C
drying time			2.0 to 4.0	hr
Temperature at the rear of the barrel			190 to 210	°C
Temperature in the middle of the barrel			200 to 220	°C
Temperature at the front of the material cylinder			210 to 230	°C
Spray nozzle temperature			210 to 240	°C
Processing (melt) temperature			210 to 240	°C
Mold temperature			40 to 60	°C
Back pressure			30.0 to 60.0	Mpa
Screw speed			30 to 80	rpm
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	1.8 MPa, Unannealed, 6.40 mm, Injection	ASTM D648	74.0	°C
Vicat softening temperature		ASTM D15255	81.0	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density	比重	ASTM D792	1.06	g/cm³
melt mass-flow rate	220°C/10.0 kg	ASTM D1238	10	g/10 min
Shrinkage rate	23°C, 3.20 mm, Injection，Flow	ASTM D955	0.40 - 0.70	%
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	R-Scale, 23°C, Injection	ASTM D785	88

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.