ABS 3453 SINOPEC SHANGHAI GAOQIAO

Form：Granules | Grade：Injection grade

Properties:

High impact resistanceHigh mobilityHigh gloss

Typical Applications:

Home appliance componentsFitness equipmentCastersAutomotive sector

Supplier(0)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Home appliance components \| Fitness equipment \| Casters \| Automotive sector
Properties:	High impact resistance \| High mobility \| High gloss

Certificates

No Data...

Technical Data Sheet

Basic Performance	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	200℃,3.8kg	ASTM D-1238	3.8	g/10min
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
tensile strength	Yield,1/8",5mm/min	ASTM D-638	43	Mpa
Impact strength of cantilever beam gap	23°C	ASTM D-256	35	kJ/m²
elongation at yield	1/8",5mm/min	ASTM D-638	3	%
Elongation at Break	1/8",5mm/min	ASTM D-638	14	%
tensile strength	1/8",5mm/min，Break	ASTM D-638	31	Mpa
Tensile modulus		ASTM D638/ISO 527	31	kg/cm²(MPa)[Lb/in²]
tensile strength		ASTM D638/ISO 527	43	kg/cm²(MPa)[Lb/in²]
elongation		ASTM D638/ISO 527	3	%
Impact strength of cantilever beam gap		ASTM D256/ISO 179	35	kg·cm/cm(J/M)ft·lb/in
Elongation at Break		ASTM D638/ISO 527	14	%
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Vicat softening temperature	1/8",50℃/hr，120℃/10hr	ASTM D-1525	103	°C
Vicat softening temperature	Vicat softening temperature		ASTM D1525/ISO R306	103	℃（℉）
Physical properties	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate		ASTM D1238/ISO 1133	5	g/10min
melt mass-flow rate	melt mass-flow rate		ASTM D1238/ISO 1133	10	g/10min

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.