PA66 70G33HS1L BK DUPONT JAPAN

Form：Granules | Grade：Enhanced level

Properties:

Thermal stabilityhigh strengthGlass fiber reinforced

Typical Applications:

Automotive sector

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Automotive sector
Properties:	Thermal stability \| high strength \| Glass fiber reinforced

Certificates

No Data...

Technical Data Sheet

Filling analysis	Test Condition	Test Method	Test Result	Test Unit
Top out temperature			210	°C
Emission of Organic Compounds		VDA 277	10.0	µgC/g
Odor		VDA 270	3.00
impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	75	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
Burning rate	1.00 mm	ISO 3795	28	mm/min
UL flame retardant rating		UL 94	HB
UL flame retardant rating	UL flame retardant rating		UL 94	HB
FMVSS combustion rate		FMVSS 302	B
雾化 - G-value (condensate)		ISO 6452	6.0E-4	g
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus		ISO 527-2	11000	Mpa
tensile strength	Break	ISO 527-2	200	Mpa
Tensile strain	Break	ISO 527-2	3.0	%
Bending modulus		ISO 178	9500	Mpa
bending strength		ISO 178	280	Mpa
injection	Test Condition	Test Method	Test Result	Test Unit
drying temperature			80	°C
Drying time - hot air dryer			2.0 to 4.0	hr
Suggested maximum moisture content			0.20	%
Processing (melt) temperature			275 to 295	°C
Melt Temperature, Optimum			285	°C
Mold temperature			70 to 120	°C
Mold Temperature, Optimum			100	°C
Maintain pressure			50.0 to 100	Mpa
Maintain pressure	Maintain pressure	Drying Recommended		yes
Hold Pressure Time			3.00	s/mm
Maximum Screw Tangential Speed			12	m/min
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/B	261	°C
Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/A	252	°C
Melting temperature		ISO 11357-3	262	°C
Linear coefficient of thermal expansion	Flow	ISO 11359-2	1.8E-5	cm/cm/°C
	Linear coefficient of thermal expansion	Flow : -40 to 23°C	ISO 11359-2	2.4E-5	cm/cm/°C
		Linear coefficient of thermal expansion	Flow : 55 to 160°C	ISO 11359-2	1.3E-5	cm/cm/°C
			Linear coefficient of thermal expansion	Across Flow	ISO 11359-2	8.3E-5	cm/cm/°C
				Linear coefficient of thermal expansion	Across Flow : -40 to 23°C	ISO 11359-2	6.5E-5	cm/cm/°C
				Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow : 55 to 160°C	ISO 11359-2	1.4E-4	cm/cm/°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate	横向Flow	ISO 294-4	1.1	%
Shrinkage rate	Shrinkage rate	Flow	ISO 294-4	0.30	%
Water absorption rate	Saturation, 23°C, 2.00 mm	ISO 62	5.7	%
Water absorption rate	Water absorption rate	Equilibrium, 23°C, 2.00 mm, 50% RH	ISO 62	1.8	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Compared to the anti leakage trace index		UL 746	PLC 1

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.