PC/ABS NS0031 SABIC INNOVATIVE US

Form：Granules | Grade：Injection grade

Properties:

High mobilityFlame retardant

Typical Applications:

CastersElectrical applications

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Casters \| Electrical applications
Properties:	High mobility \| Flame retardant

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of cantilever beam gap	23°C	ISO 180/1A	9.5	kJ/m²
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	32	kJ/m²
Dart impact	23°C,EnergyatPeakLoad	ASTM D3763	15.0	J
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile strain	Break	ISO 527-2	6.0	%
Bending modulus		ASTM D790	2990	Mpa
Bending modulus	Bending modulus		ISO 178	2800	Mpa
bending strength		ASTM D790	89.6	Mpa
bending strength	bending strength		ISO 178	86.0	Mpa
elongation	Break	ASTM D638	4.7	%
Tensile strain	Yield	ISO 527-2	3.5	%
elongation	Yield	ASTM D638	3.3	%
tensile strength	Break	ISO 527-2	46.0	Mpa
	tensile strength	Break	ASTM D638	49.6	Mpa
		tensile strength	Yield	ISO 527-2	50.0	Mpa
		tensile strength	tensile strength	Yield	ASTM D638	52.4	Mpa
Tensile modulus		ISO 527-2/1	2700	Mpa
Tensile modulus	Tensile modulus		ASTM D638	3110	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion	TD：-40to40°C	ISO 11359-2	8.2E-05	cm/cm/°C
	Linear coefficient of thermal expansion	TD：-40to40°C	ASTME831	6.3E-05	cm/cm/°C
		Linear coefficient of thermal expansion	MD：-40to40°C	ISO 11359-2	5.9E-05	cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD：-40to40°C	ASTME831	7.7E-05	cm/cm/°C
Hot deformation temperature	1.8MPa,Unannealed,64.0mmSpan	ISO 75-2/Af	103	°C
	Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	105	°C
		Hot deformation temperature	0.45MPa,Unannealed,64.0mmSpan	ISO 75-2/Bf	115	°C
		Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed,3.20mm	ASTM D648	120	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	24hr,50%RH	ASTM D570	0.10	%
Shrinkage rate	MD:24hr	ISO 294-4	0.30	%
	Shrinkage rate	TD:24hr	ISO 294-4	0.35	%
		Shrinkage rate	TD：24hr	ASTM D955	0.35	%
		Shrinkage rate	Shrinkage rate	MD：24hr	ASTM D955	0.30	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Volume resistivity		ASTM D257	1E+04	ohms·cm
Surface resistivity		ASTM D257	10to1.0E+3	ohms
Shielding effectiveness (EMI)	3.00mm	Internal Method	50to65	dB

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.