Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Water absorption rate | | ASTM D570 | 0.22 % |
| melt mass-flow rate | | ASTM D1238 | 27 g/10min |
| other | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTM D785 | M80 |
| Shrinkage rate | | | 2 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| flammability | | UL 94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ASTM D638 | 63 Mpa |
| elongation | | ASTM D638 | 40 % |
| bending strength | | ASTM D790 | 93 Mpa |
| Flexural modulus | | ASTM D790 | 2700 Mpa |
| shearing strength | | ASTM D732 | 56 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 6 kJ/m² |
| Impact strength of cantilever beam gap | | ASTM D1822 | 100 kgf·cm/cm² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| melting temperature | | DSC | 165 °C |
| Thermal stability temperature | | ASTM D648 | 158 °C |
| Thermal stability temperature | | ASTM D648 | 110 °C |
| Linear coefficient of thermal expansion | | E831 | 13 *10 -5°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.