| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | ISO 294-4 | 0.50to0.70 % |
| Water absorption rate | | ISO 62 | 0.70 % |
| Water absorption rate | | ISO 62 | 0.20 % |
| density | | ISO 1183 | 1.13 g/cm³ |
| Melt volume flow rate | | ISO 1133 | 22.0 cm³/10min |
| Shrinkage rate | | ISO 294-4 | 0.50to0.70 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO 179/1eA | 49 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 无断裂 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2/1 | 2300 MPa |
| tensile strength | Yield | ISO 527-2/50 | 56.0 MPa |
| Tensile strain | Break | ISO 527-2/50 | 5.0 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric strength | | IEC 60243-1 | 24 kV/mm |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 2 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/B | 127 °C |
| Heat distortion temperature | | ISO 75-2/A | 105 °C |
| vicat | | ISO 306/B50 | 122 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.