Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Water absorption rate | | ASTM D570 | 0.40 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTM D785 | 104 |
| Rockwell hardness | | ASTM D785 | >125 |
| Shore hardness | | ASTM D2240 | 95 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Limiting Oxygen Index | | ASTM D2863 | 58 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| bending strength | | ASTM D790 | 221 Mpa |
| Compression Modulus | | ASTM D695 | 5860 Mpa |
| compressive strength | | ASTM D695 | 393 Mpa |
| compressive strength | | ASTM D695 | 345 Mpa |
| coefficient of friction | | | 0.16 |
| coefficient of friction | | | 0.15 |
| coefficient of friction | | | 0.16 |
| coefficient of friction | | | 0.18 |
| coefficient of friction | | | 0.14 |
| coefficient of friction | | | 0.16 |
| Tensile modulus | | ASTM D638 | 5860 Mpa |
| tensile strength | | ASTM D638 | 159 Mpa |
| elongation | | ASTM D638 | 3.0 % |
| Flexural modulus | | ASTM D790 | 6550 Mpa |
| Fatigue-%ofstresstofailure | | ASTM D638 | 35 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Suspended wall beam without notch impact strength | | ASTM D256 | 590 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric constant | | ASTM D150 | 3.40 |
| dielectric constant | | ASTM D150 | 3.40 |
| dielectric constant | | ASTM D150 | 3.30 |
| Dissipation Factor | | ASTM D150 | 0.0 |
| Dissipation Factor | | ASTM D150 | 3E-03 |
| Dissipation Factor | | ASTM D150 | 0.034 |
| arc resistance | | ASTM D495 | 185 sec |
| Volume resistivity | | ASTM D257 | 2E+15 ohms·cm |
| dielectric strength | | ASTM D149 | 23 KV/mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 435 °C |
| Glass Transition Temperature | | DMA | 427 °C |
| Linear coefficient of thermal expansion | | TMA | 2.3E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | | TMA | 3.2E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | | TMA | 0.40 W/m/K |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.