Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D1505 | 0.923 g/cm³ |
| melt mass-flow rate | | ASTM D1238 | 8.0 g/10min |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | ASTM D2240 | 51 |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| gloss | | ASTM D523 | 105 |
| Haze ratio | | ASTM D1003 | 8.0 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| coefficient of friction | | ASTM D1894 | <0.060 |
| film | Test Condition | Test Method | Test Result |
|---|
| Elmendorf tear strength | | ASTM D1922 | 137.3 kN/m |
| Elmendorf tear strength | | ASTM D1922 | 78.5 kN/m |
| Secant modulus | | ASTM D882 | 186 MPa |
| Secant modulus | | ASTM D882 | 216 MPa |
| tensile strength | | ASTM D882 | 17.7 MPa |
| tensile strength | | ASTM D882 | 13.7 MPa |
| elongation | | ASTM D882 | 400 % |
| elongation | | ASTM D882 | 520 % |
| Dart impact | | ASTM D1709 | 50 g |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| vicat | | ASTM D1525 | 95.0 °C |
| Heat distortion temperature | | ASTM D648 | 50.0 °C |
| brittle temperature | | ASTM D746 | <-70.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.