Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Water absorption rate | | ASTMD570 | 0.58 % |
| Water absorption rate | | ASTMD570 | 0.35 % |
| density | | ASTMD792 | 1.20 g/cm³ |
| Water absorption rate | | ASTMD570 | 0.15 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTMD785 | 74 |
| Rockwell hardness | | ASTMD785 | 118 |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| refractive index | | ASTMD542 | 1.586 |
| transmissivity | | ASTMD1003 | 85.0到91.0 % |
| Haze ratio | | ASTMD1003 | 0.50到2.0 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ASTMD256 | 无断裂 |
| Impact strength of cantilever beam gap | | ASTMD256 | 850 J/m |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ASTMD638 | 2340 MPa |
| tensile strength | | ASTMD638 | 57.9 MPa |
| tensile strength | | ASTMD638 | 65.5 MPa |
| elongation | | ASTMD638 | 100 % |
| Flexural modulus | | ASTMD790 | 2340 MPa |
| bending strength | | ASTMD790 | 93.1 MPa |
| compressive strength | | ASTMD695 | 86.2 MPa |
| shear strength | | ASTMD732 | 40.0 MPa |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric constant | | ASTMD150 | 2.90 |
| dielectric constant | | ASTMD150 | 2.90 |
| Volume resistivity | | ASTMD257 | 1E+16 ohms·cm |
| dielectric strength | | ASTMD149 | 15 kV/mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTMD648 | 141 °C |
| Heat distortion temperature | | ASTMD648 | 135 °C |
| | ASTMD696 | 6.8E-05 cm/cm/°C |
| specific heat | | ASTMC351 | 1260 J/kg/°C |
| thermal conductivity | | ASTMC177 | 0.19 W/m/K |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.