HIPS POLYREX® PH-888H TAIWAN CHIMEI
607
- Properties:heat-resisting
- Usages:Electrical fieldElectronic fieldOffice supplies
- Certificates:ULMSDS
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | --3 | ASTMD792 | 1.05 | g/cm³ |
| 23°C | ISO1183 | 1.05 | g/cm³ | |
| Melt mass flow rate | 200°C/5.0kg | ASTMD1238 | 3.8 | g/10min |
| Melt Volume-Flow Rate (MVR) | 200°C/5.0kg | ISO1133 | 3.80 | cm3/10min |
| Shrinkage rate | ISO294-4 | 0.40到0.70 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | L计秤 | ASTMD785 | 63 | |
| tensile strength | 屈服 | ISO527-2/50 | 30.0 | Mpa |
| 断裂4 | ASTMD638 | 29.4 | Mpa | |
| 断裂 | ISO527-2/50 | 30.0 | Mpa | |
| elongation | 断裂4 | ASTMD638 | 45 | % |
| 断裂 | ISO527-2/50 | 50 | % | |
| Bending modulus | --5 | ASTMD790 | 1930 | Mpa |
| --6 | ISO178 | 1500 | Mpa | |
| bending strength | --5 | ASTMD790 | 44.1 | Mpa |
| --6 | ISO178 | 39.0 | Mpa | |
| Charpy Notched Impact Strength | -30°C | ISO179 | 5.2 | kJ/m² |
| 23°C | ISO179 | 9.0 | kJ/m² | |
| Impact strength of cantilever beam gap | 23°C,3.20mm | ASTMD256 | 97 | J/m |
| 23°C,6.40mm | ASTMD256 | 83 | J/m | |
| -30°C | ISO180/1A | 4.5 | kJ/m² | |
| 23°C | ISO180/1A | 8.0 | kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 1.8MPa,未退火 | ASTMD648 | 82.0 | °C |
| 1.8MPa,未退火 | ISO75-2/A | 79.0 | °C | |
| 1.8MPa,退火 | ASTMD648 | 97.0 | °C | |
| 1.8MPa,退火 | ISO75-2/A | 96.0 | °C | |
| vicat softening point | -- | ASTMD15257,ISO306/A507 | 102 | °C |
| -- | ISO306/B50 | 92.0 | °C | |
| Linear coefficient of thermal expansion | MD | ISO11359-2 | 4.0E-5到6.0E-5 | cm/cm/°C |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.