Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.77 g/cm³ |
| Shrinkage rate | | ASTM D955 | 0.25 % |
| Shrinkage rate | | ASTM D955 | 1.0 % |
| Water absorption rate | | ASTM D570 | 0.020 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | M-Scale | ASTM D785 | 100 |
| Rockwell hardness | R-Scale | ASTM D785 | 121 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-0 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Suspended wall beam without notch impact strength | | ASTM D256 | 550 J/m |
| Impact strength of cantilever beam gap | | ASTM D256 | 100 J/m |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| compressive strength | | ASTM D695 | 200 MPa |
| coefficient of friction | | ASTM D1894 | 0.35 |
| coefficient of friction | | ASTM D1894 | 0.35 |
| Tensile modulus | | ASTM D638 | 18000 MPa |
| tensile strength | | ASTM D638 | 180 MPa |
| elongation | Break | ASTM D638 | 1.4 % |
| Flexural modulus | | ASTM D790 | 17000 MPa |
| bending strength | | ASTM D790 | 270 MPa |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ASTM D257 | 1E+16 ohms·cm |
| dielectric strength | | ASTM D149 | 16 kV/mm |
| dielectric constant | | ASTM D150 | 4.50 |
| Dissipation Factor | | ASTM D150 | 4E-03 |
| arc resistance | | ASTM D495 | 125 sec |
| Compared to the Leakage Tracking Index (CTI) | | UL 746 | PLC 4 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 265 °C |
| Linear coefficient of thermal expansion | | ASTM D696 | 2E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.