PC 3025 Dongguan Hairui

Form：Powder | Grade：General injection grade

Supplier(0)

Product Description

Certificates(0)

Datasheet

Product Description

Form:

Pellets

Certificates

No Data...

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result	Test Unit
Fuzzy coefficient (Haze)		ISO 14782	10	%
Transmittance rate		ASTM D1003/ISO 13468	0	%
Refractive index		ASTM D542/ISO 489	00
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Elongation at Break		ASTM D638/ISO 527	12	%
Tensile modulus		ASTM D638/ISO 527	1500	kg/cm²(MPa)[Lb/in²]；
tensile strength		ASTM D638/ISO 527	45	kg/cm²(MPa)[Lb/in²]；
elongation		ASTM D638/ISO 527	12	%
Bending modulus		ASTM D790/ISO 178	60	kg/cm²(MPa)[Lb/in²]；
bending strength		ASTM D790/ISO 178	60	kg/cm²(MPa)[Lb/in²]；
Izod Notched Impact Strength		ASTM D256/ISO 179	16	kg·cm/cm(J/M)ft·lb/in
Charpy Notched Impact Strength		ASTM D256/ISO 179	16	kg·cm/cm(J/M)ft·lb/in
Charpy Notched Impact Strength	Charpy Notched Impact Strength		ASTM D256/ISO 179	10	kg·cm/cm(J/M)ft·lb/in
Tensile elongation at break (elongation at break)		ASTM D638/ISO 527	12	%
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Combustibility (rate)		UL94	1.32
Hot deformation temperature		ASTM D648/ISO 75	125	℃（℉）
melting point			230-260	℃（℉）
Vicat softening temperature		ASTM D1525/ISO R306	125	℃（℉）
Linear coefficient of thermal expansion		ASTM D696/ISO 11359	12	mm/mm.℃
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Molding shrinkage rate		ASTM D955	0.3-0.6	%
density		ASTM D792/ISO 1183	1.4
Melt index (flow coefficient)		ASTM D1238/ISO 1133	15	g/10min
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Surface resistivity		ASTM D257/IEC 60093	0000	Ω
Dielectric constant		ASTM D150/IEC 60250	10
Dielectric constant	Dielectric constant		ASTM D150/IEC 60250	12
Dielectric loss		ASTM D150/IEC 60250	12
Arc resistance		ASTM D495/IEC 60112	000
Volume resistivity		ASTM D257/IEC 60093	12	Ω.cm

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.