Technical Data Sheet
physical property | Test Condition | Test Method | Test Result |
---|
Water absorption rate | | ISO 62 | 0.24 % |
Shrinkage rate | | | 0.50 % |
density | | ISO 1183 | 1.21 g/cm³ |
hardness | Test Condition | Test Method | Test Result |
---|
Shore hardness | | | 80 |
flammability | Test Condition | Test Method | Test Result |
---|
UL flame retardant rating | | | Yes. |
Hot filament ignition temperature | | IEC 60695-2-13 | 960 °C |
UL flame retardant rating | | UL 94 | V-0 |
Impact resistance | Test Condition | Test Method | Test Result |
---|
Impact strength of simply supported beam without notch | | ISO 179 | 无断裂 |
Charpy Notched Impact Strength | | ISO 179 | 8.0 kJ/m² |
Impact strength of simply supported beam without notch | | ISO 179 | 无断裂 |
Mechanical properties | Test Condition | Test Method | Test Result |
---|
Tensile modulus | | ISO 527-2 | 2300 MPa |
Tensile strain | Break | ISO 527-2 | >50 % |
tensile strength | Yield | ISO 527-2 | 66.0 MPa |
Electrical performance | Test Condition | Test Method | Test Result |
---|
Surface Resistivity | | IEC 60093 | <1.0E+15 ohms |
Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 3 |
Thermal performance | Test Condition | Test Method | Test Result |
---|
vicat | | ISO 306 | 145 °C |
Heat distortion temperature | | ISO 75-2/A | 125 °C |
Heat distortion temperature | | ISO 75-2/B | 140 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.