ABS HI-12 BASF GERMANY

219

Form：Granules | Grade：Injection grade

Properties:

High mobilityHigh impact resistance

Typical Applications:

Household daily necessitiesWashing machineKitchen utensilsElectrical applicationsElectrical/Electronic ApplicationsHelmetElectrical appliances

Supplier(1)

Product Description

Certificates(1)

Datasheet

Alternative(1)

Product Description

Typical Applications:	Household daily necessities \| Washing machine \| Kitchen utensils \| Electrical applications \| Electrical/Electronic Applications \| Helmet \| Electrical appliances
Properties:	High mobility \| High impact resistance

Certificates

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Charpy Notched Impact Strength	-30°C	ISO 179	11	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179	30	kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179	160	kJ/m²
Impact strength of cantilever beam gap	23°C	ISO 180/A	31	kJ/m²
	Impact strength of cantilever beam gap	-30°C	ISO 180/A	11	kJ/m²
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ASTM D256	35.0	kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179	无断裂
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	3.2mm	UL 94	HB
UL flame retardant rating	UL flame retardant rating	1.6mm	UL 94	HB
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength		ISO 178	58.0	Mpa
Tensile modulus		ISO 527-2	1900	Mpa
tensile strength	Yield,23°C	ISO 527-2	40.0	Mpa
Tensile strain	Yield,23°C	ISO 527-2	2.7	%
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Maximum operating temperature			80	°C
thermal conductivity		DIN 52612	0.17	W/m/K
Linear coefficient of thermal expansion	MD	ISO 11359-2	8.0E-5到1.1E-4	cm/cm/°C
Vicat softening temperature	--	ISO 306/B50	96.0	°C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/A50	104	°C
Hot deformation temperature	1.8MPa,Annealed	ISO 75-2/A	97.0	°C
Hot deformation temperature	Hot deformation temperature	0.45MPa,Annealed	ISO 75-2/B	102	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.21	%
Water absorption rate	Water absorption rate	Saturation,23°C	ISO 62	1.0	%
Shrinkage rate		ISO 294-4	0.40-0.70	%
Melt Volume Flow Rate (MVR)	220°C/10.0kg	ISO 1133	14.0	cm3/10min
density		ISO 1183	1.02	g/cm³
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Dissipation factor	1MHz	IEC 60250	8.2E-03
Dissipation factor	Dissipation factor	100Hz	IEC 60250	5.4E-03
Dielectric constant	1.00mm,1MHz		2.80
Dielectric constant	Dielectric constant	100Hz	IEC 60250	2.90
Volume resistivity		IEC 60093	1E+15	ohms·cm
Compared to the anti leakage trace index		IEC 60112	PLC 0
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	R-Sale	ISO 2039-2	101
Ball Pressure Test		ISO 2039-1	80.0	Mpa

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.