| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ISO1133 | 6.0 g/10min |
| Shrinkage rate | | ASTMD955 | 0.20到0.60 % |
| Water absorption rate | | ISO62 | 0.30 % |
| density | | ISO1183 | 1.18 g/cm³ |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | M-Scale | ASTMD785 | 96 |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| refractive index | | ISO489 | 1.490 |
| transmissivity | | ASTMD1003 | 92.0 % |
| Haze ratio | | ASTMD1003 | 0.50 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile stress | | ISO527-2 | 70.0 MPa |
| Tensile strain | | ISO527-2 | 6.0 % |
| Flexural modulus | | ISO178 | 3300 MPa |
| Bending stress | | ISO178 | 103 MPa |
| compression stress | | ISO604 | 110 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO179/2C | 2.0 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO179/2U | 11 kJ/m² |
| Impact strength of cantilever beam gap | | ISO180/1A | 1.8 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | ASTMD257 | >1.0E+14 ohms |
| Volume resistivity | | ASTMD257 | >1.0E+15 ohms·cm |
| dielectric strength | | ASTMD149 | 20 kV/mm |
| Dissipation Factor | | ASTMD150 | 0.040 |
| dielectric constant | | ASTMD150 | 3.70 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO75-2/A | 95.0 °C |
| vicat | | ISO306/B | 103 °C |
| | ASTMD696 | 6.5E-05 cm/cm/°C |
| specific heat | | | 2090 J/kg/°C |
| Heat distortion temperature | | ISO75-2/B | 100 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.