PA6 CBI 15 NATURAL
0
- Properties:Glass bead 15%filler by weightimproved impact resistance
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shrinkage rate | 0.60 | ||
| Water absorption rate | ISO 62 | 0.20 % | |
| ash content | ISO 3451 | 14 to 16 % | |
| density | ISO 1183 | 1.17 to 1.19 g/cm³ | |
| Shrinkage rate | ISO 294-4 | 0.90 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Hardness (Shore) | ISO 868 | 80 to 82 | |
| Tensile modulus | ISO 527-2 | 3500 to 4500 MPa | |
| tensile strength | ISO 527-2 | 75.0 to 90.0 MPa | |
| Tensile strain | ISO 527-2 | 3.5 to 4.5 % | |
| Flexural modulus | ISO 178 | 3000 to 4000 MPa | |
| bending strength | ISO 178 | 80.0 to 100 MPa | |
| Charpy Notched Impact Strength | ISO 179/1eA | 6.0 to 9.0 kJ/m² | |
| Impact strength of cantilever beam gap | ISO 180/1A | 6.0 to 9.0 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Hot deformation temperature (HDT) | ISO 75-2/B | 200 ℃ | |
| ISO 75-2/A | 195 | ||
| vicat | ISO 306/B | 200 ℃ | |
| melting temperature | ISO 3146 | 215 to 225 ℃ | |
| UL flame retardant rating | UL 94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.