PC 3207 550115 COVESTRO THAILAND

Form：Granules | Grade：UV resistant grade

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Certificates

No Data...

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result	Test Unit
transmissivity	1000 μm	ISO 13468-2	89.0	%
	transmissivity	2000 μm	ISO 13468-2	89.0	%
		transmissivity	3000 μm	ISO 13468-2	88.0	%
		transmissivity	transmissivity	4000 μm	ISO 13468-2	88.0	%
turbidity	3000 μm	ISO 14782	0.20	%
impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	-60°C	ISO 179/1eU	无断裂
	Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	无断裂
	Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	无断裂
Impact strength of cantilever beam gap	-30°C, Complete Break	ISO 180/A	20	kJ/m²
	Impact strength of cantilever beam gap	-20°C, Partial Break	ISO 180/A	71	kJ/m²
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C, Partial Break	ISO 180/A	75	kJ/m²
Multi axis Instrumented Impact Energy	23°C	ISO 6603-2	60.0	J
Multi axis Instrumented Peak Impact Force	23°C	ISO 6603-2	5720	N
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus	23°C	ISO 527-2/1	2270	Mpa
tensile strength	Yield, 23°C	ISO 527-2/50	62.0	Mpa
Tensile strain	Yield, 23°C	ISO 527-2/50	6.5	%
Tensile strain	Tensile strain	Break, 23°C	ISO 527-2/5	68	%
Nominal tensile fracture strain	23°C	ISO 527-2/5	> 50	%
Bending modulus	23°C	ISO 178	2400	Mpa
bending strength	23°C	ISO 178	97.0	Mpa
bending strength	bending strength	3.5% Strain, 23°C	ISO 178	72.0	Mpa
injection	Test Condition	Test Method	Test Result	Test Unit
Drying Temperature - Dry Air Dryer			120	°C
Drying time - Dry Air Dryer			4.0	hr
Suggested maximum moisture content			< 0.020	%
Suggested injection volume			30 to 70	%
Temperature at the rear of the barrel			250 to 270	°C
Temperature in the middle of the barrel			270 to 290	°C
Temperature at the front of the material cylinder			285 to 305	°C
Spray nozzle temperature			270 to 305	°C
Processing (melt) temperature			290 to 330	°C
Mold temperature			70 to 110	°C
Back pressure			10.0 to 20.0	Mpa
Exhaust hole depth			0.025 to 0.075	mm
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/B	141	°C
Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/A	130	°C
Glass transition temperature		ISO 11357-2	151	°C
Vicat softening temperature	--	ISO 306/B50	149	°C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	150	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Melt Volume Flow Rate (MVR)	300°C/1.2 kg	ISO 1133	4.00	cm3/10min
Shrinkage rate	横向Flow : 2.00 mm	ISO 294-4	0.73	%
Shrinkage rate	Shrinkage rate	Flow : 2.00 mm	ISO 294-4	0.73	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.