Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.14 |
| density | | ASTM D792 | 1.14 g/cm³ |
| Shrinkage rate | | | 0.50to0.70 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | R-Scale | ASTM D785 | 108 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ASTM D638 | 580 kgf/cm2 |
| elongation | | ASTM D638 | 120 % |
| tensile strength | | ASTM D790 | 750 kgf/cm2 |
| Flexural modulus | | ASTM D790 | 21000 kgf/cm2 |
| Impact strength of cantilever beam gap | | ASTM D256 | 70 kgf.cm/cm |
| Rockwell hardness | | ASTM D786 | 108 R |
| tensile strength | | ASTM D638 | 56.9 MPa |
| elongation | Break | ASTM D638 | 120 % |
| Flexural modulus | | ASTM D790 | 2260 MPa |
| bending strength | | ASTM D790 | 78.5 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 640 J/m |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 110 ℃ |
| UL flame retardant rating | | UL 94 | HB |
| Heat distortion temperature | | ASTM D648 | 110 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare