Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.20 g/cm³ |
| melt mass-flow rate | | ASTM D1238 | 22 g/10min |
| Shrinkage rate | | ASTM D955 | 0.50to0.70 % |
| Water absorption rate | | ASTM D570 | 0.23 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | M-Scale | ASTM D785 | 75 |
| Rockwell hardness | R-Scale | ASTM D785 | 120 |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| refractive index | | ASTM D542 | 1.586 |
| transmissivity | | ASTM D1003 | 89.0 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Hot filament ignition temperature | | IEC 60695-2-13 | 850 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Flexural modulus | | ASTM D790 | 2350 MPa |
| bending strength | | ASTM D790 | 90.0 MPa |
| Tensile modulus | | ASTM D638 | 2300 MPa |
| tensile strength | Yield | ASTM D638 | 63.0 MPa |
| tensile strength | Break | ASTM D638 | 68.0 MPa |
| elongation | Break | ASTM D638 | 90 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 640 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ASTM D257 | >1.0E+16 ohms·cm |
| dielectric constant | | ASTM D150 | 2.91 |
| dielectric constant | | ASTM D150 | 2.85 |
| Dissipation Factor | | ASTM D150 | 6.6E-04 |
| Dissipation Factor | | ASTM D150 | 9.2E-03 |
| arc resistance | | ASTM D495 | 100to120 sec |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 128 °C |
| Linear coefficient of thermal expansion | | ASTM D696 | 6.5E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.