TPU-Est/eth

TPU-Est/eth DP R 9918 geba Kunststoffcompounds GmbH

Compare

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	22 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	45 kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	无断裂
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	无断裂

mechanical properties	Test Condition	Test Method	Test Result
Bending modulus	23°C	ISO 178	1800 MPa
bending strength	-30°C	ISO 178	118 MPa
bending strength	bending strength	23°C	ISO 178	54.0 MPa
tensile strength		ISO 527-2/200	59.0 MPa
Tensile strain	Break	ISO 527-2/200	17 %
Bending modulus	-30°C	ISO 178	3000 MPa
Wear resistance		ISO 4649	80 mm³

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	167 °C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	126 °C
Vicat softening temperature		ISO 306/B50	92.0 °C
Linear coefficient of thermal expansion	MD	DIN 53752	1E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD	DIN 53752	1.1E-04 cm/cm/°C

Physical properties	Test Condition	Test Method	Test Result
density		ISO 1183/A	1.29 g/cm³
Shrinkage rate	TD		0.32 %
Shrinkage rate	Shrinkage rate	MD		0.10 %

hardness	Test Condition	Test Method	Test Result
Shore hardness	ShoreD	ISO 868	64

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.